Structural! spectroscopic analyses and H-2/O-2/CO responses of thulium(III) oxide nanosquare sheets

Title
Structural! spectroscopic analyses and H-2/O-2/CO responses of thulium(III) oxide nanosquare sheets
Author(s)
손영구이성우[이성우]박성균[박성균]강준길[강준길]민봉기
Keywords
DOPED GERMANATE GLASSES; INFRARED UP-CONVERSION; NANOPARTICLES; EMISSION; NANOCRYSTALS; TM2O3; TM3+; PHOTOLUMINESCENCE; COMPOUND; POWDER
Issue Date
201407
Publisher
ELSEVIER SCIENCE BV
Citation
APPLIED SURFACE SCIENCE, v.307, pp.736 - 743
Abstract
Cubic (space group Ia 3, a-10.49 angstrom) bixbyite two-dimensional thulium(III) oxide nanosquare structure was first prepared, and then fully characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction crystallography (XRD), thermogravimetric analysis/differential scanning calorimetry (TGA/DSC), UV-vis-near IR absorption, Raman, X-ray photoelectron spectroscopy, temperature-programmed reduction and oxidation experiments. The crystal structure was fully refined, and detailed structural parameters were determined on the basis of the Rietveld analysis. High resolution TEM image revealed interplanar distances of 0.26 nm and 0.31 nm corresponding to the (4 0 0) and (2 2 2) planes, respectively. The structure projections of the (4 0 0) and (2 2 2) planes were imaged along [0 1 1] and [1 1 -2] directions, respectively. A broad H-2 reduction peak and a sharp 02 oxidation peak were found at 688 C and 123 degrees C, respectively. CO oxidation activity started to appear at 400-500 degrees C. The new results of this study further highlight the characteristics and the actual applications of Tm(III) oxide. (c) 2014 Elsevier B.V. All rights reserved.
URI
http://hdl.handle.net/YU.REPOSITORY/31495http://dx.doi.org/10.1016/j.apsusc.2014.04.149
ISSN
0169-4332
Appears in Collections:
이과대학 > 화학생화학부 > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE