Effect of the magnetization process on low-field microwave absorption by FeBN magnetic thin film

Title
Effect of the magnetization process on low-field microwave absorption by FeBN magnetic thin film
Author(s)
김기현이준식김진우
Keywords
POWER ABSORPTION
Issue Date
201408
Publisher
WILEY-V C H VERLAG GMBH
Citation
PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, v.211, no.8, pp.1900 - 1902
Abstract
The magnetization process of a typical soft magnetic film was examined using ferromagnetic resonance (FMR) measurements on 9.84 GHz. A 500-nm-thick Fe85.9B2.6N11.5 film with in-plane uniaxial magnetic anisotropy was deposited by RF sputtering. The saturation magnetization and coercivity of the FeBN magnetic film were 17.3 kG and 2.4 Oe, respectively, at the hard direction. The microwave absorption signals showed two different absorption peaks: small signals at a near zero dc field and at a high dc field. The resonance magnetic fields for the major and minor peaks were observed at 532 and 604 Oe, respectively. The g-factor obtained was 2.15. The uniaxial magnetic anisotropy field was approximately 14 Oe by vibrating sample magnetometer, which coincided with that of the FMR results. The absorption at a low-field revealed different characteristics from those of conventional FMR absorption. The magnetic anisotropy field obtained by low-field microwave absorption was approximately 13.5 Oe, which is comparable to that of the FMR and VSM results. (C) 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
URI
http://hdl.handle.net/YU.REPOSITORY/31260http://dx.doi.org/10.1002/pssa.201330451
ISSN
1862-6300
Appears in Collections:
이과대학 > 물리학과 > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE