Mixture of fuels approach for the solution combustion synthesis of LaAlO3 nanopowders

Title
Mixture of fuels approach for the solution combustion synthesis of LaAlO3 nanopowders
Author(s)
김기현제야슬란챤드라다스
Keywords
LANTHANUM ALUMINATE; LOW-TEMPERATURE; POWDER; GEL
Issue Date
201003
Publisher
ELSEVIER SCIENCE BV
Citation
ADVANCED POWDER TECHNOLOGY, v.21, no.2, pp.100 - 105
Abstract
A modified solution combustion approach was used in the preparation of nanosize LaAlO3 (similar to 23.6 nm) using mixture of citric acid and oxalic acid as fuels with corresponding metal nitrates. The synthesized and calcined powders were characterized by Fourier transform infra red spectrometry (FTIR), Differential thermal analysis-Thermogravimetry analysis (DTA-TGA), X-ray diffractometry (XRD) and Transmission electron microscopy (TEM). The FTIR spectra show the lower frequency bands at 656 and 442 cm(-1) corresponds to metal-oxygen bonds (possible La-O and Al-O stretching frequencies) vibrations for the perovskite structure compound. DTA confirms the formation temperature of LaAlO3 varies between 830-835 C. XRD results show that mixture of fuels ratio is influential on the crystallite size of the resultant powders. The average particle size of LaAlO3-1 as determined from TEM was about 41 nm, whereas for LaAlO3-2 and LaAlO3-3 samples, particles are seriously aggregated. (C) 2009 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.
URI
http://hdl.handle.net/YU.REPOSITORY/22798http://dx.doi.org/10.1016/j.apt.2009.10.014
ISSN
0921-8831
Appears in Collections:
이과대학 > 물리학과 > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE