쉘 스택 주조 3.60wt%C-2.60wt%Si 조성 구상흑연주철의 Normalizing 및 Quenching 처리 시 기계적 성질에 미치는 합금 원소의 영향

Title
쉘 스택 주조 3.60wt%C-2.60wt%Si 조성 구상흑연주철의 Normalizing 및 Quenching 처리 시 기계적 성질에 미치는 합금 원소의 영향
Other Titles
Effects of Alloying Elements on the Mechanical Properties of Normalized and Quenched 3.60wt%C-2.60wt%Si Ductile Cast Irons Poured into Shell Stack Mold
Author(s)
권해욱김효민[김효민]여인동[여인동]남원식[남원식]
Keywords
Cast iron; Heat-treatment; Alloying element; Stack molding; Mechanical properties.
Issue Date
201004
Publisher
한국주조공학회
Citation
한국주조공학회지, v.30, no.2, pp.66 - 75
Abstract
The effects of alloying elements on the mechanical properties of normalized and quenched 3.60wt%C-2.60wt%C ductile cast iron poured into shell stack mold were investigated. The strength and hardness of as-cast specimen were increased and the elongation of it was decreased with the additions of Mn, Cu and Sn. The strength and hardness were increased with the addition of 0.40wt%Mo and then rather decreased with the increased addition of 0.80wt%. The strength and hardness were increased with normalizing treatment and the strengths of normalized specimens were increased slightly with the addition of alloying elements except Mo. Meanwhile the yield strength of the normalized specimen was increased slightly with the addition of Mo, the tensile strength was not changed much. Meanwhile the hardness and strength of the quenched specimen were slightly increased with the addition of Mn, those were almost not changed with the amount added. The tensile strength of the quenched specimen with larger diameter,when the Cu had been added, and the tensile and yield strengths of them, when Mo had been added, were increased with the addition of alloying element. On the other hand, those were not changed with the amount added. For the case of specimen with smaller diameter, there were no effects of these two elements. When Sn had been added, the strength of hardened specimen with larger diameter was slightly increased with the amount added. However, that with smaller diameter was rather decreased with it. The effect of specimen diameter on the strength of quenched specimen with the addition of Cu, Mo and Sn was reduced.
URI
http://hdl.handle.net/YU.REPOSITORY/22517
ISSN
1598-706X
Appears in Collections:
공과대학 > 신소재공학부 > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE